BX-SRE-303 Epoxy modified methyl phenyl silicone emulsion
This Epoxy modified methyl phenyl silicone emulsion is a non-ionic, epoxy-modified methyl/phenyl resin emulsion designed for heat-resistant industrial coatings. It offers excellent high-temperature resistance and decorative coating performance. The varnish can withstand temperatures up to 300 °C, while colored paints remain stable up to 500 °C. It demonstrates good compatibility with organic resins and can achieve effective room-temperature self-drying when combined with water-based curing agents. The emulsion can be easily diluted with water for application.
Ⅰ. Product Details
| Item | Index | Test method |
| Appearance | Milky white liquid | GB1721 |
| Viscosity(4#cup, S) | 25-40 | GB1723 |
| Solid content(150℃, 2h), % | 50±2 | GB1725 |
| Epoxy value (Effective solid content) | 0.06-0.16 | GB/T1677-2008 |
| Note: The above data are for reference only and are not guaranteed technical specifications. *Corrections & supplements: 1. “Mike white” is revised to “Milky white” (standard description for opaque white liquid appearance); 2. “Expoxy value” is corrected to “Epoxy value” (standard terminology for resin performance indicators); 3. Referenced GB/GB/T standards are Chinese National Standards, where GB1721 specifies paint appearance testing, GB1723 specifies coating viscosity testing, GB1725 specifies coating solid content testing, and GB/T1677-2008 specifies epoxy value testing methods for epoxy resins. | ||
Ⅱ. Recommend applications
It can be used in industrial heat resistant paint applications, suitable for the industry requiring salt spray resistance, such as ship steam pipeline etc.
Ⅲ. Packaging and Storage
Generally 200KG, 50KG plastic bucker packaging; Stored sealed in a cool and dry environment at 5~36℃. Shelf life is generally 6 months from the date of production.
Ⅳ. Instructions
It is suggested to prepare water – based resin -free color paste, and then use it with resin emulsion together. When compounding with organic resins (such as water Sexual polyamide curing agent), it is necessary to screen the compatibility of the two components, especially in varnish application. Resin emulsion has better room temperature self-drying property, it can give the workpiece early protection and transport performance. But if you want to get good heat resistance and physical and mechanical properties, it is recommended to cure at 200- 280℃ for 15-60min,for example, 250℃ for 30 minutes or 280℃ for 15 minutes.